IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishInternal friction (IF) and dynamic modulus measurements on a high nitrogen (0.8 wt%) austenitic steel in the temperature range from room temperature to 800 °C have been carried out by using a vibrating reed technique with electrostatic excitation and frequency modulation detection of flexural vibrations in the frequency range of kHz. The IF spectrum of the as-prepared material shows a broad peak superimposed to an exponentially increasing background. The discontinuous precipitation of Cr2N phase changes the characteristics of the peak. The results have been discussed by considering interstitial-substitutional (i-s) interactions.
| Autori: | |
| Autori: | Deodati, P; Montanari, R; Rovatti, L; Ucciardello, N; Carosi, A |
| Titolo: | Anelastic phenomena and Cr2N precipitation in a high nitrogen austenitic steel |
| Nome del convegno: | THERMEC2009 |
| Luogo del convegno: | BERLINO |
| Anno del convegno: | 2009 |
| Rilevanza: | Rilevanza internazionale |
| Sezione: | contributo |
| ???metadata.dc.date.created???: | 2009 |
| Data di pubblicazione: | 2010 |
| Settore Scientifico Disciplinare: | Settore ING-IND/21 - Metallurgia |
| Lingua: | English |
| Tipologia: | Intervento a convegno |
| Citazione: | Deodati, P., Montanari, R., Rovatti, L., Ucciardello, N., & Carosi, A. (2010). Anelastic phenomena and Cr2N precipitation in a high nitrogen austenitic steel. Paper presented at THERMEC2009, BERLINO. |