Electron beam (EB) welding has been used to realize the seams on 2 mm thick plates of directionally solidified (DS) IN792 superalloy. A grid of the samples has been prepared by varying the pass speed v from 1 to 2.5 m/min, while the other process parameters (power P = 1 kW, acceleration voltage T = 50 kV, beam current I = 20 mA) were kept constant. Experiments were carried out both at room temperature and with pre-heating at 200 °C or 300 °C. Once found the best process conditions (pre-heating at 300 °C; v = 2.5 m/min) the effect of postwelding heat treatments at 700 and 750 °C for increasing time up to 2 hours has been investigated.
Barbieri, G., Soltani, P., Kaciulis, S., Montanari, R., Varone, A. (2017). IN792 DS superalloy: Optimization of EB welding and post-welding heat treatments. In Materials Science Forum (pp.175-180). Trans Tech Publications Ltd [10.4028/www.scientific.net/MSF.879.175].
IN792 DS superalloy: Optimization of EB welding and post-welding heat treatments
Soltani P.;Montanari R.;Varone A.
2017-01-01
Abstract
Electron beam (EB) welding has been used to realize the seams on 2 mm thick plates of directionally solidified (DS) IN792 superalloy. A grid of the samples has been prepared by varying the pass speed v from 1 to 2.5 m/min, while the other process parameters (power P = 1 kW, acceleration voltage T = 50 kV, beam current I = 20 mA) were kept constant. Experiments were carried out both at room temperature and with pre-heating at 200 °C or 300 °C. Once found the best process conditions (pre-heating at 300 °C; v = 2.5 m/min) the effect of postwelding heat treatments at 700 and 750 °C for increasing time up to 2 hours has been investigated.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.