AISI 304 steel with a biphasic structure ('+), induced by plastic deformation at room temperature, shows an anomalous evolution of martensite content when heated at 400°C. High-temperature X-ray diffraction (XRD) has been used to investigate the phenomenon. Isothermal measurements at 400°C for times up to 2.0 x 104 s show that martensite progressively transforms to austenite but an increase of martensite content is observed after cooling to room temperature. The result confirms that the heat treatment causes composition inhomogeneities and a local increase of MS (martensite start temperature) in the zones depleted of alloying elements so that a certain amount of martensite can form during cooling to room temperature. The temperature range of martensitic transformation is 240-190 °C and was determined by dynamic modulus measurements.

Gauzzi, F., Montanari, R., Principi, G., Tata, M.e. (2006). AISI 304 steel: anomalous evolution of martensitic phase following heat treatments at 400°C. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 438-440, 202-206 [10.1016/j.msea.2006.02.116].

AISI 304 steel: anomalous evolution of martensitic phase following heat treatments at 400°C

GAUZZI, FRANCO;MONTANARI, ROBERTO;TATA, MARIA ELISA
2006-01-01

Abstract

AISI 304 steel with a biphasic structure ('+), induced by plastic deformation at room temperature, shows an anomalous evolution of martensite content when heated at 400°C. High-temperature X-ray diffraction (XRD) has been used to investigate the phenomenon. Isothermal measurements at 400°C for times up to 2.0 x 104 s show that martensite progressively transforms to austenite but an increase of martensite content is observed after cooling to room temperature. The result confirms that the heat treatment causes composition inhomogeneities and a local increase of MS (martensite start temperature) in the zones depleted of alloying elements so that a certain amount of martensite can form during cooling to room temperature. The temperature range of martensitic transformation is 240-190 °C and was determined by dynamic modulus measurements.
2006
Pubblicato
Rilevanza internazionale
Articolo
Sì, ma tipo non specificato
Settore ING-IND/21 - METALLURGIA
English
Con Impact Factor ISI
Gauzzi, F., Montanari, R., Principi, G., Tata, M.e. (2006). AISI 304 steel: anomalous evolution of martensitic phase following heat treatments at 400°C. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 438-440, 202-206 [10.1016/j.msea.2006.02.116].
Gauzzi, F; Montanari, R; Principi, G; Tata, Me
Articolo su rivista
File in questo prodotto:
File Dimensione Formato  
lavoro mat sci eng 2006.pdf

accesso aperto

Dimensione 502.84 kB
Formato Adobe PDF
502.84 kB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2108/51200
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? 20
social impact