Core transitions from the Al 2p level in amorphous and crystalline Al2O3

The soft-X-ray spectra of aluminium oxide in the polycrystalline and amorphous forms have been investigated in detail with improved resolution using the synchrotron radiation of the Frascati electron synchrotron. In contrast to a previous measurement, it is found that the L2,3 threshold starts at almost the same energy in both forms. The sharp peaks observed at the absorption edge are interpreted as excitons. This picture fits well both with ESCA results and with the optical spectra at the fundamental edge in the ultraviolet. It is suggested that metastable excitons are responsible for the intense structure observed at (82.6 ± 0.3) eV in the ordered phase and lacking in the amorphous phase. The spectral features of crystalline alumina are analyzed on the basis of the band structure. The modifications induced by the lack of long-range order in the amorphous samples are discussed thoroughly. Kous avons étudié en détail les spectres d'absorption X de l'oxyde d'aluminium dans les formes polycristalline et amorphe avec meilleur résolution qu'auparavant, employant la radiation émise par l'éléctrosynchrotron de Fraseati. On a trouvé, è la différence des mesures précédentes, que les transitions L2,3 commencent presque à la měme énergie dans les deux formes. Le pics étroits obsérvés on été interprété commes des excitons. Cette interprétation s'accorde soit avec les résultats d'ESCA soit avec les spectres optiques prés de l'absorption fondamentale dans l'ultraviolet. On pense que des excitons métastables peuvent expliquer les structures obsérvés à (82,6 ± 0,3) eV dans la phase ordonnée et manquantes dans la phase amorphe. Les spectres de l'alumine cristalline sont examinées suivant la structure des bandes. Les modifications dues à l'absence d'ordre cristallin à grandes distances dans les substances amorphes sont discutées.