Experimental Set-Up of the Production Process and Mechanical Characterization of Metal Foams Manufactured by Lost-PLA Technique with Different Cell Morphology

A flexible and versatile method for manufacturing open-cell metal foams, called lost- PLA, is presented in this work. With a double extruder 3D printer (FDM, Ultimaker S3, Utrecht, The Netherlands), it is possible to make polymer-based samples of the lost model. Through CAD modeling, different geometries were replicated so as to get black PLA samples. This method combines the advantages of rapid prototyping with the possibility of manufacturing Al-alloy specimens with low time to market. The production process is articulated in many steps: PLA foams are inserted into an ultra-resistant plaster mix, after which the polymer is thermally degraded. The next step consists of the gravity casting of the EN-6082 alloy in the plaster form, obtaining metal foams that are interesting from a technological point of view as well as with respect to their mechanical properties. These foam prototypes can find application in the automotive, civil and aeronautical fields due to their high surface/weight ratio, making them optimal for heat exchange and for the ability to absorb energy during compression. The main aspects on which we focus are the set-up of the process parameters and the characterization of the mechanical properties of the manufactured samples. The main production steps are examined at first. After that, the results obtained for mechanical performance during static compression tests with different geometry porosities are compared and discussed. The foam with truncated octahedron cells was found to show the highest absorbed energy/relative density ratio.