CoFe2O4/multiwall carbon nanotubes (MWCNTs) composite nanofibers were produced by electrospinning a dispersion of MWCNTs in a solution of polyvinylpyrrolidone, iron(III) nitrate nonahydrate, cobalt (II) acetate tetrahydrate, absolute ethanol and H2O. Microstructure was examined by scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HR-TEM). Thermal behaviour was studied by thermogravimetry and differential thermal analysis (TG-DTA) and phase analysis of calcined fibers was performed by X-ray diffraction (XRD). Upon thermal treatment at 450 °C defect-free, randomly oriented composite fibers having a mean diameter of 60 ± 10 nm were obtained. The results show that the presence of MWCNTs does not affect the spinel cubic phase formation.
Lamastra, F., Nanni, F., Camilli, L., Matassa, R., Carbone, M., Gusmano, G. (2010). Morphology and structure of electrospun CoFe2O4/multi-wall carbon nanotubes composite nanofibers. CHEMICAL ENGINEERING JOURNAL, 162(1), 430-435 [10.1016/j.cej.2010.05.025].
Morphology and structure of electrospun CoFe2O4/multi-wall carbon nanotubes composite nanofibers
Lamastra, FR;NANNI, FRANCESCA;Camilli, L;CARBONE, MARILENA;
2010-01-01
Abstract
CoFe2O4/multiwall carbon nanotubes (MWCNTs) composite nanofibers were produced by electrospinning a dispersion of MWCNTs in a solution of polyvinylpyrrolidone, iron(III) nitrate nonahydrate, cobalt (II) acetate tetrahydrate, absolute ethanol and H2O. Microstructure was examined by scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HR-TEM). Thermal behaviour was studied by thermogravimetry and differential thermal analysis (TG-DTA) and phase analysis of calcined fibers was performed by X-ray diffraction (XRD). Upon thermal treatment at 450 °C defect-free, randomly oriented composite fibers having a mean diameter of 60 ± 10 nm were obtained. The results show that the presence of MWCNTs does not affect the spinel cubic phase formation.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.