Mismatched or shadowed individual cells in a module can operate in the reverse bias (RB) regime. We investigate and identify key mechanisms for RB operation and degradation in dye solar cells (DSCs). Currentvoltage characteristics in RB are sensitive to the type of dye utilised and to TiCl4 substrate treatment. Subjecting the cell to a RB of 0.4 V over 740 h has little effect on conversion efficiency whereas a significant lowering is observed for the harsher stress tests at 0.6 V and by forcing a constant current equal to its ISC. For more prolonged reverse biases at ISC (>740 h), we show that depletion of [I3-] inside the DSC can lead the reverse bias potentials across the cells to considerably increase in time. Electrochemical impedance measurements show that the overpotentials at the counter electrodes (CEs) can eventually reach values high enough to cause hydrogen evolution. Clear evidence of gas bubbles forming inside a complete dye solar cell under reverse bias stress, leading to severe device degradation, is presented. We also show that reactions of iodine with water present in the electrolyte can play an important role in [I3-] depletion and in the formation of hydrogen at the Pt CE.

Mastroianni, S., Lembo, A., Brown, T.m., Reale, A., DI CARLO, A. (2012). Electrochemistry in Reverse Biased Dye Solar Cells and Dye/Electrolyte Degradation Mechanisms. CHEMPHYSCHEM, 13(12), 2964-2975 [10.1002/cphc.201200229].

Electrochemistry in Reverse Biased Dye Solar Cells and Dye/Electrolyte Degradation Mechanisms

Lembo, A;BROWN, THOMAS MEREDITH;REALE, ANDREA;DI CARLO, ALDO
2012-01-01

Abstract

Mismatched or shadowed individual cells in a module can operate in the reverse bias (RB) regime. We investigate and identify key mechanisms for RB operation and degradation in dye solar cells (DSCs). Currentvoltage characteristics in RB are sensitive to the type of dye utilised and to TiCl4 substrate treatment. Subjecting the cell to a RB of 0.4 V over 740 h has little effect on conversion efficiency whereas a significant lowering is observed for the harsher stress tests at 0.6 V and by forcing a constant current equal to its ISC. For more prolonged reverse biases at ISC (>740 h), we show that depletion of [I3-] inside the DSC can lead the reverse bias potentials across the cells to considerably increase in time. Electrochemical impedance measurements show that the overpotentials at the counter electrodes (CEs) can eventually reach values high enough to cause hydrogen evolution. Clear evidence of gas bubbles forming inside a complete dye solar cell under reverse bias stress, leading to severe device degradation, is presented. We also show that reactions of iodine with water present in the electrolyte can play an important role in [I3-] depletion and in the formation of hydrogen at the Pt CE.
2012
Pubblicato
Rilevanza internazionale
Articolo
Esperti anonimi
Settore ING-INF/01 - ELETTRONICA
English
Mastroianni, S., Lembo, A., Brown, T.m., Reale, A., DI CARLO, A. (2012). Electrochemistry in Reverse Biased Dye Solar Cells and Dye/Electrolyte Degradation Mechanisms. CHEMPHYSCHEM, 13(12), 2964-2975 [10.1002/cphc.201200229].
Mastroianni, S; Lembo, A; Brown, Tm; Reale, A; DI CARLO, A
Articolo su rivista
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2108/104731
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 35
  • ???jsp.display-item.citation.isi??? 31
social impact