Different Cr- and Ti-base films were deposited using PVD-arc deposition onto WC-Co substrates, and multilayered coatings were obtained from the superimposition of diamond coatings, deposited on the PVD interlayer using hot filament chemical vapour deposition (HFCVD). The behaviour of PVD-arc deposited CrN and CrC interlayers between diamond and WC-Co substrates was studied and compared to TiN, TiC, and Ti(C,N) interlayers. Tribological tests with alternative sliding motion were carried out to check the multilayer (PVD+ diamond) film adhesion on WC-Co substrate. Multilayer films obtained using PVD arc, characterised by large surface droplets, demonstrated good wear resistance, while diamond deposited on smooth PVD TiN films was not adherent. Multilayered Ti(C,N)+diamond film samples generally showed poor wear resistance. Diamond adhesion on Cr-based PVD coatings deposited on WC-Co substrate was good. In particular, CrN interlayers improved diamond film properties and 6 gm-thick diamond films deposited on CrN showed excellent wear behaviour characterised by the absence of measurable wear volume after sling tests. Good diamond adhesion on Cr-based PVD films has been attributed to chromium carbide formation on PVD film surfaces during the CVD process. (c) 2005 Elsevier B.V. All rights reserved.
Polini, R., Mantini, F., Barletta, M., Valle, R., Casadei, F. (2006). Hot filament chemical vapour deposition and wear resistance of diamond films on WC-Co substrates coated using PVD-arc deposition technique. DIAMOND AND RELATED MATERIALS, 15(9), 1284-1291 [10.1016/j.diamond.2005.09.045].
Hot filament chemical vapour deposition and wear resistance of diamond films on WC-Co substrates coated using PVD-arc deposition technique
POLINI, RICCARDO
;BARLETTA, MASSIMILIANO;
2006-01-01
Abstract
Different Cr- and Ti-base films were deposited using PVD-arc deposition onto WC-Co substrates, and multilayered coatings were obtained from the superimposition of diamond coatings, deposited on the PVD interlayer using hot filament chemical vapour deposition (HFCVD). The behaviour of PVD-arc deposited CrN and CrC interlayers between diamond and WC-Co substrates was studied and compared to TiN, TiC, and Ti(C,N) interlayers. Tribological tests with alternative sliding motion were carried out to check the multilayer (PVD+ diamond) film adhesion on WC-Co substrate. Multilayer films obtained using PVD arc, characterised by large surface droplets, demonstrated good wear resistance, while diamond deposited on smooth PVD TiN films was not adherent. Multilayered Ti(C,N)+diamond film samples generally showed poor wear resistance. Diamond adhesion on Cr-based PVD coatings deposited on WC-Co substrate was good. In particular, CrN interlayers improved diamond film properties and 6 gm-thick diamond films deposited on CrN showed excellent wear behaviour characterised by the absence of measurable wear volume after sling tests. Good diamond adhesion on Cr-based PVD films has been attributed to chromium carbide formation on PVD film surfaces during the CVD process. (c) 2005 Elsevier B.V. All rights reserved.File | Dimensione | Formato | |
---|---|---|---|
DRM_2006_15_1284.pdf
solo utenti autorizzati
Descrizione: Articolo principale
Tipologia:
Versione Editoriale (PDF)
Licenza:
Copyright dell'editore
Dimensione
2.15 MB
Formato
Adobe PDF
|
2.15 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.