This paper deals with the study of the laser marking process of titanium cold sprayed coatings on aluminium substrates. Despite several studies regarding the laser marking process are available in literature very few attention have been paid to the marking of cold sprayed coatings and there are no previous papers in literature. Also the phenomena occurring during the marking of a porous coating are to date not fully understood and will be discussed in this paper. The experimental campaign was also repeated on grade 2 titanium rolled sheets with a thickness of 2 mm. The marking tests were carried out under different experimental conditions varying the main process parameters (i.e. laser pulse power and laser scan speed), after that the mark sections were observed by optical microscope and SEM. Both the maximum penetration depth and width of the marks were acquired and also internal damages induced by the process were studied. A correlation between the process parameters and the mark's geometry was found. The results show the effectiveness of the laser process to produce high quality marks on both the titanium layer and the titanium sheet. Moreover, a higher mark penetration on Ti coating was observed compared to the Ti sheet. However, the results show also the possibility to introduce severe and hidden damages in both materials if the process parameters are not properly set.

Astarita, A., Genna, S., Leone, C., Memola Capece Minutolo, F., Squillace, A., Velotti, C. (2016). Study of the laser marking process of cold sprayed titanium coatings on aluminium substrates. OPTICS AND LASER TECHNOLOGY, 83, 168-176 [10.1016/j.optlastec.2016.04.007].

Study of the laser marking process of cold sprayed titanium coatings on aluminium substrates

GENNA, SILVIO;
2016-01-01

Abstract

This paper deals with the study of the laser marking process of titanium cold sprayed coatings on aluminium substrates. Despite several studies regarding the laser marking process are available in literature very few attention have been paid to the marking of cold sprayed coatings and there are no previous papers in literature. Also the phenomena occurring during the marking of a porous coating are to date not fully understood and will be discussed in this paper. The experimental campaign was also repeated on grade 2 titanium rolled sheets with a thickness of 2 mm. The marking tests were carried out under different experimental conditions varying the main process parameters (i.e. laser pulse power and laser scan speed), after that the mark sections were observed by optical microscope and SEM. Both the maximum penetration depth and width of the marks were acquired and also internal damages induced by the process were studied. A correlation between the process parameters and the mark's geometry was found. The results show the effectiveness of the laser process to produce high quality marks on both the titanium layer and the titanium sheet. Moreover, a higher mark penetration on Ti coating was observed compared to the Ti sheet. However, the results show also the possibility to introduce severe and hidden damages in both materials if the process parameters are not properly set.
2016
Pubblicato
Rilevanza internazionale
Articolo
Esperti anonimi
Settore ING-IND/16 - TECNOLOGIE E SISTEMI DI LAVORAZIONE
English
Con Impact Factor ISI
http://www.sciencedirect.com/science/article/pii/S0030399216300627?via%3Dihub
Astarita, A., Genna, S., Leone, C., Memola Capece Minutolo, F., Squillace, A., Velotti, C. (2016). Study of the laser marking process of cold sprayed titanium coatings on aluminium substrates. OPTICS AND LASER TECHNOLOGY, 83, 168-176 [10.1016/j.optlastec.2016.04.007].
Astarita, A; Genna, S; Leone, C; Memola Capece Minutolo, F; Squillace, A; Velotti, C
Articolo su rivista
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2108/188988
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 25
  • ???jsp.display-item.citation.isi??? 21
social impact