In the present work the influence of accelerated mineral carbonation on the leaching behaviour of basic oxygen furnace steel slag was investigated. The environmental behaviour of the material as evaluated through the release of major elements and toxic metals under varying pH conditions was the main focus of the study. Geochemical modelling of the eluates was used to derive a theoretical description of the underlying leaching phenomena for the carbonated material as compared to the original slag. Among the investigated elements, Ca and Si were most appreciably affected by carbonation. A very clear effect of carbonation on leaching was observed for silicate phases, and lower-Ca/Si-ratio minerals were found to control leaching in carbonated slag eluates as compared to the corresponding untreated slag sample as a result of Ca depletion from the residual slag particles. Clear evidence was also gained of solubility control for Ca, Mg and Mn by a number of carbonate minerals, indicating a significant involvement of the original slag constituents in the carbonation process. The release of toxic metals (Zn, V, Cr, Mo) was found to be variously affected by carbonation, owing to different mechanisms including pH changes, dissolution/precipitation of carbonates as well as sorption onto reactive mineral surfaces. The leaching test results were used to derive further considerations on the expected metal release levels on the basis of specific assumptions on the relevant pH domains for the untreated and carbonated slag.

Costa, G., Polettini, A., Pomi, R., Stramazzo, A. (2016). Leaching modelling of slurry-phase carbonated steel slag. JOURNAL OF HAZARDOUS MATERIALS, 302(January 2016), 415-425 [10.1016/j.jhazmat.2015.10.005].

Leaching modelling of slurry-phase carbonated steel slag

COSTA, GIULIA;
2016-01-01

Abstract

In the present work the influence of accelerated mineral carbonation on the leaching behaviour of basic oxygen furnace steel slag was investigated. The environmental behaviour of the material as evaluated through the release of major elements and toxic metals under varying pH conditions was the main focus of the study. Geochemical modelling of the eluates was used to derive a theoretical description of the underlying leaching phenomena for the carbonated material as compared to the original slag. Among the investigated elements, Ca and Si were most appreciably affected by carbonation. A very clear effect of carbonation on leaching was observed for silicate phases, and lower-Ca/Si-ratio minerals were found to control leaching in carbonated slag eluates as compared to the corresponding untreated slag sample as a result of Ca depletion from the residual slag particles. Clear evidence was also gained of solubility control for Ca, Mg and Mn by a number of carbonate minerals, indicating a significant involvement of the original slag constituents in the carbonation process. The release of toxic metals (Zn, V, Cr, Mo) was found to be variously affected by carbonation, owing to different mechanisms including pH changes, dissolution/precipitation of carbonates as well as sorption onto reactive mineral surfaces. The leaching test results were used to derive further considerations on the expected metal release levels on the basis of specific assumptions on the relevant pH domains for the untreated and carbonated slag.
2016
Pubblicato
Rilevanza internazionale
Articolo
Esperti anonimi
Settore ICAR/03 - INGEGNERIA SANITARIA - AMBIENTALE
English
Con Impact Factor ISI
Accelerated carbonation; Geochemical modelling; Metal leaching; Steelmaking slag
Costa, G., Polettini, A., Pomi, R., Stramazzo, A. (2016). Leaching modelling of slurry-phase carbonated steel slag. JOURNAL OF HAZARDOUS MATERIALS, 302(January 2016), 415-425 [10.1016/j.jhazmat.2015.10.005].
Costa, G; Polettini, A; Pomi, R; Stramazzo, A
Articolo su rivista
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/2108/186927
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 30
  • ???jsp.display-item.citation.isi??? 25
social impact