Precursor effects of indium melting have been investigated by means of Mechanical Spectroscopy (MS) and High Temperature X-ray Diffraction (HT-XRD). MS tests evidenced a sharp drop of dynamic modulus in the temperature range between 418 K and 429 K (melting point). At 429 K, HT-XRD showed partial grain re-orientation, peak profile broadening, in particular in the lower part, and peak shift towards lower angles. Experimental results are consistent with density increase of self-interstitials and vacancies in the crystal lattice before melting. Self-interstitials and vacancies play a synergic role in the solid–liquid (S-L) transformation. The increase of self-interstitials over a temperature range of about 10 K before melting has the effect of weakening interatomic bonds (modulus drop) that favors the successive vacancy formation. Finally, the huge increase of vacancy concentration above 428 K leads to the collapse of crystal lattice (melting).
Precursor effects of indium melting have been investigated by means of Mechanical Spectroscopy (MS) and High Temperature X-ray Diffraction (HT-XRD). MS tests evidenced a sharp drop of dynamic modulus in the temperature range between 418 K and 429 K (melting point). At 429 K, HT-XRD showed partial grain re-orientation, peak profile broadening, in particular in the lower part, and peak shift towards lower angles. Experimental results are consistent with density increase of self-interstitials and vacancies in the crystal lattice before melting. Self-interstitials and vacancies play a synergic role in the solid-liquid (S-L) transformation. The increase of self-interstitials over a temperature range of about 10 K before melting has the effect of weakening interatomic bonds (modulus drop) that favors the successive vacancy formation. Finally, the huge increase of vacancy concentration above 428 K leads to the collapse of crystal lattice (melting).
Montanari, R., Varone, A. (2015). Synergic role of self-interstitials and vacancies in Indium melting. METALS, 5(2), 1061-1072 [10.3390/met5021061].
Synergic role of self-interstitials and vacancies in Indium melting
MONTANARI, ROBERTO;Varone, A.
2015-01-01
Abstract
Precursor effects of indium melting have been investigated by means of Mechanical Spectroscopy (MS) and High Temperature X-ray Diffraction (HT-XRD). MS tests evidenced a sharp drop of dynamic modulus in the temperature range between 418 K and 429 K (melting point). At 429 K, HT-XRD showed partial grain re-orientation, peak profile broadening, in particular in the lower part, and peak shift towards lower angles. Experimental results are consistent with density increase of self-interstitials and vacancies in the crystal lattice before melting. Self-interstitials and vacancies play a synergic role in the solid-liquid (S-L) transformation. The increase of self-interstitials over a temperature range of about 10 K before melting has the effect of weakening interatomic bonds (modulus drop) that favors the successive vacancy formation. Finally, the huge increase of vacancy concentration above 428 K leads to the collapse of crystal lattice (melting).File | Dimensione | Formato | |
---|---|---|---|
Synergic role of self-interstitials and vacancies in indium melting.pdf
accesso aperto
Licenza:
Copyright dell'editore
Dimensione
831.84 kB
Formato
Adobe PDF
|
831.84 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.